CFRP Impregnation Resin XQ-TJ
Low-viscosity epoxy resin for wet lay-up impregnation of carbon fiber fabrics. Excellent wetting and penetration, self-leveling on horizontal surfaces.
- Low viscosity for full fiber wetting
- Tensile strength ≥ 40 MPa (neat resin)
- Excellent adhesion to concrete substrate
- Transparent — visual inspection of air voids
- Room-temperature cure
Technical Specifications
| Tensile Strength (Resin) | ≥ 40 MPa |
| Elastic Modulus (Resin) | ≥ 2,500 MPa |
| Bond Strength | ≥ 2.5 MPa (concrete failure) |
| Viscosity | 1,000–3,000 mPa·s at 25°C |
| Mix Ratio | A:B = 2:1 (by weight) |
| Pot Life | 45 min at 25°C |
| Packaging | 5 kg / 15 kg set |
Applications
Carbon fiber wet lay-upCFRP laminationFabric impregnation
Related Products
Steel Bonding Adhesive XQ-JG
Two-component epoxy adhesive for bonding steel plates to concrete structures. High shear and peel strength, excellent durability in humid and marine environments.
CFRP Plate Bonding Adhesive XQ-PB
Thixotropic paste adhesive specifically formulated for bonding pultruded CFRP plates to concrete substrates. Non-sag on overhead applications.
Ready to Strengthen Your Next Project?
Get expert guidance and competitive quotes from our engineering team.