Carbon Fiber Epoxy Adhesive from reliable China adhesive manufacturers, suppliers, factory.
Carbon Fiber FRP Laminate Strip Epoxy Adhesive
Item# CarbonEpox340
Mixing Ratio: 3:1
Adopted with modified epoxy resin, CarbonEpox 340 is a new two component adhesive which has features as bonding with all kinds of base materials (cements, stones, bricks etc.), metal and steel plates, fast curing, high strength, strong anchoring, good acid and alkaline resistance, aging resistance, etc. Widely used for bonding and reinforcement for concrete with stone and steel plates, as well as all kinds of section units. Good stability within expected period, suitable for heavy section units.
Range of Application
Reinforcement for all kinds building structures, and steel bonding reinforcement of walls, floors, beams and poles etc.
Anchoring reinforcement for water conservancy facilities, docks, roads, bridges and other projects
Repairing and reinforcement for all building of industry and residence, bridge, tunnel, etc.
Features
1. Two component, modified epoxy rein, fast curing at room temperature, good bonding strength, stable mechanical properties
2. Free base layer adhesive, easy to handle and reduces the effect of construction technology on mechanical properties;
3. Can be used in wide temperature range, no precipitation;
4. For bonding between same or different materials of metal, ceramics, plastic, rubber, wood etc.
5. Excellent thixotropic performance, easy to paint and avoid hollowing and waste;
6. Good acid and alkali resistance, aging resistance, low moisture sensitivity;
Product performance
1. Basic parameters
1) Appearence
Part A (main): White cream
Part B (hardener): Black cream
2) Mixed Viscosity: 10-12 Pa.s
3) Hardened density: 1.50±0.10g/cm3
4) Mixing ratio: 3:1
5) Available handling time: (25℃): ≥30min
6) Shelf time: 24 months
Main Performance
|
Testing project |
Condition |
Index |
|
Gel performance |
||
|
Tensile Strength |
Under (23±2)℃、(50±5)%RH, tested by loading speed of 2mm/min |
≥30 Mpa |
|
Tensile modulus of elasticity |
≥3.2×103 MPa |
|
|
Elongation |
≥1.2% |
|
|
Bending Strength |
≥45Mpa (no fragmental damage) |
|
|
Compressive Strength |
≥65 Mpa |
|
|
Bonding Capacity |
||
|
Steel-Steel Tensile Shear Strength |
≥15 Mpa |
|
|
Steel-Steel bonding tensile strength |
(23±2)℃ (50±5)%RH |
≥33 Mpa |
|
Steel-Steel T-peeling strength |
(23±2)℃、(50±5)%RH |
≤25 mm (Concrete cohesion damage) |
|
Steel to C45 Concrete cohesive haul strength |
|
≥2.5 Mpa |
|
Transformation under heating |
|
≥65℃ |
|
Non-volatile content |
(105±2)℃、(180±5)min |
≥99% |
Remarks: all the values in the sheet is average.
Processing Flow
Positioning → Base materials treatment → Cleaning → Mixing the adhesive → Painting → Anchoring → Maintenance
1, positioning: mark the steel bonding position;
2, Base material treatment: Remove the painting layer on concrete surface and to drill derust and polish the steel;
3, Cleaning: using compressed air to blow the surface from dust, clean with acetone;
4, Mixing the adhesive: according to the weight ratio of A:B=3:1, weigh and mix in the barrel;
5, Painting: paint the above mixed adhesive onto the surface of concrete and steel plate, do not have bubbles inside;
6, Anchoring: attach the steel plate directly on the surface of coated concrete, remove the surrounding excess adhesive,then fix with steel frame;
7, Maintenance: fix for conservation at room temperature no less than 24 hours.
Packaging and Logistics
1. Two components in separate package, A:B=3:1 20kgs/steel bucket, 60kgs/set
2. Shall be stored in cool (under 25℃), dry and ventilated place, not exceed 1 year.
3. This product is not dangerous goods, can be shipped as normal chemical materials.
Attention
Must wear glove, mask and other safety products during processing.
If touched by skin, please treated by using acetone in first and then washed by water.
Do not use too much each time.
Steel bucket : 3.7L/5.0L/10L/18L/20L Plastic bucket: 4L/5L/10L/15L/20L