XQ-602 Epoxy Anchor Adhesive

3head-602

XQ-602 Anchoring Adhesive

Adopted with modified epoxy resin, XQ-602 Anchoring Adhesive is a two-component curing system under normal temperature, It has features of fast-curing, high strength, aging resistance, anti-acid and alkali, excellent fatigue resistance and so on, are widely used for steel, screw, anchor bolt and metal sectional materials which anchored and reinforced with concrete, rock and brick wall etc.

Range of Application

Steel bar embedding and anchor reinforcement with many building structures.
Anchoring of equipment Foundation
Anchor supporting for roof and wall of mine roadway
Anchoring for Water Conservancy facilities, docks, roads, bridges and other projects
Installation anchoring for curtain wall and chemical equipment, pipeline, billboards,etc.

Features

  1. Two component, fast curing at room temperature
  2. Stress-free fixed with small edge spacing
  3. Fast loading capacity to building structure with high adhesion, planting steel bar with embedding effect;
  4. Suitable for concrete, stone, metal and other building material;
  5. Can be proceeded under -5~45℃ temperature conditions or with water.
  6. The processing is easy without flow, good technical performance.
  7. High acid and alkali resistance, ageing resistance, good thermal performance.

Proudct performance

1. Basic parameters
1) Appearence
Part A (main): white cream
Part B (hardener): black cream
2) Mixed Viscosity: 18-22Pa.s
3) Hardened density: 1.60±0.10g/cm3
4) Shelf time: 18 months

 

Testing project  Condition Index
Gel Performance
Splitting Tensile Strength Under (23±2)℃、(50±5)%RH, tested by loading speed of 2mm/min ≥8.5 Mpa
Bending Strength ≥50 Mpa

(no fragmental damage)

Compressive Strength ≥60 Mpa
 Bonding Capacity
Steel-Steel Tensile Shear Strength (23±2)℃、(50±5)%RH ≥10 Mpa
Bonding strength of Ribbed steel bar (or screw) with concrete under constrain drawing condition (23±2)℃ (50±5)%RH C30,Ф25,L=150mm ≥11 Mpa
C60,Ф25,L=150mm ≥17 Mpa
Steel-Steel T-peeling strength (23±2)℃、(50±5)%RH ≤25 mm
Non-volatile content (105±2)℃、(180±5)min ≥99 %

 

 
Temperarure ℃ -5 0 10 20 ≥30
Operation time (min) 60 45 30 25 20
Harden time (h) 72 48 24 12 6

 

Packaging and Logistics

  1.  Two components in seperate plastic barrel, 20kgs/set and 60kgs/set
  2. Shall be stored in cool (under 25℃), dry and ventilated place, not exceed 1 year.
  3.  Toxic free, non dangerous, can be shipped as normal chemical materials.